[1]张开宇,孙齐磊*,种溪,等.新型复配阻锈剂的电化学性能研究[J].山东建筑大学学报,2019,34(03):57-61.[doi:10.12077/sdjz.2019.03.009]
 ZHANG Kaiyu,SUN Qilei*,CHONG Xi,et al.Study on electrochemical properties of new composite inhibitor in simulated concrete solution[J].Journal of Shandong jianzhu university,2019,34(03):57-61.[doi:10.12077/sdjz.2019.03.009]
点击复制

新型复配阻锈剂的电化学性能研究()
分享到:

《山东建筑大学学报》[ISSN:1673-7644/CN:37-1449/TU]

卷:
34
期数:
2019年03期
页码:
57-61
栏目:
研究论文
出版日期:
2019-06-15

文章信息/Info

Title:
Study on electrochemical properties of new composite inhibitor in simulated concrete solution
文章编号:
1673-7644(2019)03-0057-05
作者:
张开宇孙齐磊*种溪英鲁军南洪友
(山东建筑大学 材料科学与工程学院,山东 济南 250101)
Author(s):
ZHANG Kaiyu SUN Qilei* CHONG Xi et al.
(School of Material Science and Engineering, Shandong Jianzhu University, Jinan 250101, China)
关键词:
阻锈剂自然电位法极化曲线电化学阻抗谱
Keywords:
corrosion inhibitor spontaneous potential method polarization curve electrochemical impedance spectroscopy
分类号:
TG113.23
DOI:
10.12077/sdjz.2019.03.009
文献标志码:
A
摘要:
添加阻锈剂可以有效防止或减轻钢筋锈蚀,但目前使用的阻锈剂大多含有亚硝酸盐,不仅污染环境而且会使后期稳定性变差,开发高性能、低成本、环保无污染的新型阻锈剂可为钢筋防腐研究的发展提供新的途径。文章通过复配得到一种新型阻锈剂,利用电化学方法研究了加入氯化钠的混凝土模拟液中钢筋的阻锈性能,运用极化曲线和电化学阻抗谱等手段分析了阻锈剂的作用原理,并与钼酸盐和醇类阻锈剂进行对比。结果表明:当新型复配阻锈剂掺量为4wt%时,其对钢筋的阻锈效果最佳;新型复配阻锈剂能同时抑制钢筋表面的阴极和阳极反应,阻锈效果更加稳定;复配得到的新型阻锈剂具有良好的效果。
Abstract:
Adding corrosion inhibitors can effectively prevent or reduce the corrosion of steel bars, but most of the corrosion inhibitors currently used contain nitrite, which will cause environmental pollution. The development of new corrosion inhibitors with high performance, low cost and environmental protection can provide a new way for the development of anti-corrosion research of steel bars. In this paper, a new corrosion inhibitor was obtained by combination. The effect of corrosion inhibitor on reinforcing steel bar was studied by electrochemical test and analysis method after adding NaCl concrete simulation solution. The mechanism of inhibitor was analyzed by polarization curve and electrochemical impedance spectroscopy, and compared with molybdate and alcohols. The results show that the new compound rust inhibitor has a good effect; when the mass fraction of the new compound rust inhibitor is 4%, the effect of the new compound rust inhibitor is the best; the new compound rust inhibitor can inhibit the cathode and anode reaction on the surface of the steel bar at the same time, and the effect of the new compound rust inhibitor is more stable. The experimental results indicate that the corrosion inhibitor can form a dense molecular film on the surface of reinforcing steel bar. Compared with molybdate and alcohol corrosion inhibitors, it has longer action time, more stable rust inhibition effect, and is an environmentally friendly rust inhibitor.

参考文献/References:

[1]贾红梅,阎贵平,闫光杰.混凝土中钢筋锈蚀的研究[J].中国安全科学学报, 2005, 15(5):56-59.[2]Xu K. Corrosion inhibitors and other protective systems in concrete repair concepts or misconnects[J]. Cement & Concrete Composites, 2004, 26(3):255-263.[3]Hansson C M, Mammoliti L, Hope B B. Corrosion inhibitors in concrete-part I: the principles[J]. Cement & Concrete Research,1998,28(12):1775-1781.[4]Liu Z Y, Zhou X G, Li X L. Effect of migrating corrosion inhibitor on corrosion rate of reinforcing steel in concrete with various admixed chloride[J]. Applied Mechanics & Materials,2012,204-208:3146-3150.[5]曹攀,周婷婷,白秀琴,等.深海环境中的材料腐蚀与防护研究进展[J].中国腐蚀与防护学报, 2015,35(1):12-20.[6]陈云翔,冯丽娟,蔡建宾,等.新型复配阻锈剂在混凝土模拟液和试块中对钢筋锈蚀的抑制[J].中国腐蚀与防护学报,2018,38(4):37-44.[7]Morris W, Vázquez M. A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides[J]. Cement & Concrete Research, 2002, 32(2):259-267.[8]Jamil H E, Shriri A, Boulif R, et al. Corrosion behaviour of reinforcing steel exposed to an amino alcohol based corrosion inhibitor[J].Cement & Concrete Composites,2005,27(6):671-678. [9]马世豪,李伟华,郑海兵,等.钢筋阻锈剂的阻锈机理及性能评价的研究进展[J].腐蚀与防护, 2017,8(12):963-968.[10]陶蕾,郑书忠,秦立娟,等.电化学测试技术在缓蚀剂缓蚀行为研究中的应用[J].工业水处理, 2010,30(8):1-5.[11]陈飞,解利昕,孙晨,等.动电位极化曲线法研究铝合金材料在海水中腐蚀现象[J].天津化工,2014,28(5):12-14.[12]陈舒恬,马文亮,王珏,等.采用极化曲线法研究GH4700合金的耐蚀性[J].现代冶金,2015(1):5-8.[13]王晓彤,孙丛涛,程火焰.氨基醇类阻锈剂的阻锈机理[J].硅酸盐通报,2017,36(1):84-88.[14]张鹤,刘宗玉.醇胺类有机物对混凝土模拟孔溶液中钢筋的阻锈作用研究[J].混凝土,2014(5):87-90.[15]原梦晓.迁移型阻锈剂在混凝土中的阻锈性能及迁移性能研究[D].青岛:青岛理工大学, 2016.