[1]张思峰,*,陈兴吉,等.岩土预应力锚索腐蚀损伤演化规律研究[J].山东建筑大学学报,2018,(06):1-6.[doi:10.12077/sdjz.2018.06.001]
 Zhang Sifeng,*,Chen Xingji,et al.Study on corrosion damage evolution mechanism of geotechnical prestressed anchor cable[J].Journal of Shandong jianzhu university,2018,(06):1-6.[doi:10.12077/sdjz.2018.06.001]
点击复制

岩土预应力锚索腐蚀损伤演化规律研究()
分享到:

《山东建筑大学学报》[ISSN:1673-7644/CN:37-1449/TU]

卷:
期数:
2018年06期
页码:
1-6
栏目:
研究论文
出版日期:
2018-12-01

文章信息/Info

Title:
Study on corrosion damage evolution mechanism of geotechnical prestressed anchor cable
文章编号:
1673-7644(2018)06-0001-06
作者:
张思峰1*陈兴吉1韩冰2齐辉2
(1. 山东建筑大学 交通工程学院,山东 济南 250101;2. 齐鲁交通发展集团有限公司,山东 济南 250101)
Author(s):
Zhang Sifeng1* Chen Xingji1 Han Bing2et al.
(1. School of Transportation Engineering, Shandong Jianzhu University, Jinan 250101, China; 2. Qilu Transportation Development Group, Jinan 250101, China)
关键词:
岩土预应力锚索腐蚀损伤演化机理
Keywords:
geotechnical prestressed anchorage cable corrosion damage evolution mechanism
分类号:
TU511
DOI:
10.12077/sdjz.2018.06.001
文献标志码:
A
摘要:
研究应力腐蚀对岩土预应力锚索长期耐久性的影响可以有效减少应力腐蚀重要环节。文章基于室内腐蚀试验,利用超景深三维数字显微系统对预应力索体在不同腐蚀时间下的锈蚀损伤形貌进行了观测,采用蚀坑面积、深度、长轴长度等指标作为其表面腐蚀损伤的统计参数,通过函数描述了参数指标与时间的关系,分析了应力腐蚀的表观损伤演化规律;利用热场发射扫描电子显微镜对索体显微组织、裂纹萌生及其发展规律进行观测,从微观结构层面探求腐蚀损伤演化的力学本质。结果表明:在腐蚀介质环境中蚀坑长轴长度、面积随时间呈指数关系,平均腐蚀深度与时间呈幂函数关系,酸性腐蚀介质更有助于腐蚀坑槽的贯通;随腐蚀时间延长,预应力锚索试件的屈服和断裂荷载均逐渐减小,到达屈服点时试件所产生的位移也有所减小;随腐蚀时间延长,材料的塑性降低,脆性逐渐增强;酸性溶液中腐蚀时间较长的试件在拉伸破坏时易表现出应力腐蚀的特征。
Abstract:
Stress corrosion has become the principal factor that can affect the longterm durability of geotechnical pestressed anchorage cable.Based on indoor corrosion test, the appearance of rust damage of the prestressed cable under different corrosion time was accurately observed by using the super depth 3D digital microscope system. The parameters such as area, depth and long axis length of the corrosion pit were used as statistical parameters of the surface corrosion damage. The correlation function was used to describe the relationship between the above parameters and time in order to analyze the apparent damage evolution rule of stress corrosion.At the same time, Scanning Electron Microscopy was used to observe the microstructure of the cable and crack initiation and development rules, in order to explore the mesomechanical nature of corrosion damage evolution from the mesostructure level. The results show that the length of the long axis and the area of the etching pits grow exponentially with time in the environments of corrosive media. The average corrosion depth is a power function of time. The yield load and the fracture load of bar are gradually decreases, and when it arrives at the yield point bar displacement also decreases. The plasticity of the material decreases and the brittleness gradually increases with the extension of corrosion time. The specimens with long corrosion time in acid solution are prone to show the feature of stress corrosion when specimens are subjected to tensile failure test.

参考文献/References:

[1]张思峰,宋修广,周健,等.预应力锚固结构耐久性及其二次加固技术研究\[J\].公路交通科技,2008,25(2):30-33.[2]杨启贵,高大水,吴海斌.对我国岩土预应力锚索防腐措施和标准的探讨\[J\].岩土工程学报,2007,29(10):1558-1562.[3]李英勇,张顶立,张宏博,等.边坡加固中预应力锚索失效机制与失效效应研究\[J\].岩土力学,2010,31(1):144-150,157.[4]程良奎,韩军,张培文.岩土锚固工程的长期性能与安全评估\[J\].岩石力学与工程学报,2008,27(5):865-872. [5]朱尔玉,王冰伟,周勇政,等.酸雨对预应力体系腐蚀的试验研究\[J\].水利学报,2012,43(11):1365-1372.[6]郑静,曾辉辉,朱本珍.腐蚀对锚索力学性能影响的试验研究\[J\].岩石力学与工程学报,2010,29(12):2469-2474.[7]罗小勇,李政.无粘结预应力钢绞线锈蚀后力学性能研究\[J\].铁道学报,2008,30(2):108-112.[8]吴振,龙跃,章陈瀑.持荷状态下钢绞线腐蚀及性能退化研究\[J\].广西工学院学报,2011,22(1):23-26,34.[9]李应勇,张思峰,王松根,等.预应力锚固结构腐蚀介质作用下的耐久性实验研究[J].岩土力学与工程学报,2008,27(8):1626-1633.[10]黎慧珊.预应力锚索腐蚀规律及耐久性研究\[D\].邯郸:河北工程大学,2017.[11]张未林.疲劳荷载与腐蚀耦合作用下岩土预应力锚固结构长期耐久性研究\[D\].济南:山东建筑大学,2017.[12]刘元康,陈惟珍,徐俊,等.拉索劣化性能研究[J].公路,2004(9):28-32.[13]陈惟珍,于振华.桥梁预应力筋损伤机理及实例研究\[J\].结构工程师,2011,27(5):37-43.[14]曾辉辉,朱本珍,高志华.强腐蚀环境下锚索强度指标及表观特性试验研究\[J\].水利与建筑工程学报,2011,9(2):48-52.[15]崔约贤,王长利.金属断口分析\[M\].哈尔滨:哈尔滨工业大学出版社,2006.[16]李富民,袁迎曙,樊登辉.预应力钢绞线的腐蚀材料学特性\[C\].乌鲁木齐:第十届后张预应力学术交流会,2008.

备注/Memo

备注/Memo:
收稿日期:2018-09-10基金项目:国家自然科学基金项目(41372300,51108252);齐鲁交通发展集团有限公司科技计划项目(JHLYDKY3)作者简介:张思峰(1976-),男,教授,博士,主要从事路基边坡加固等方面的研究.Email:sddxzsf@163.com[*通讯作者]
更新日期/Last Update: 2018-10-16